Resist 86
High-volume solids inorganic zinc ethyl silicate primer with 85% zinc dust for severe corrosive environments. Provides very good corrosion protection in atmospheric conditions and is heat resistant up to 540°C. Fast dry-to-recoat and dry-to-handle. NORSOK M-501 pre-qualified. Complies with ASTM D520 type II zinc dust.
Key Features
Technical Specifications
Product Properties
- Volume Solids
- 67 ± 2%
- VOC (EU Directive)
- 509 g/l
- Density
- 2.6 kg/l
- Flash Point
- 14°C
Film Build
- Dry Film Thickness (DFT)
- 50–90 μm
- Gloss Level
- Matt (0–35 GU @ 60°)
Application
- Mixing Ratio
- 8:2.6 (Comp A : Jotun Zinc 100 Comp B)
- Thinner
- Jotun Thinner No. 4 / No. 25 (max 5%)
- Airless Spray
- Nozzle 17–21 thou, 100 bar / 1400 psi
- Pot Life
- 8h @ 23°C
Drying Times (23°C)
- Drying Schedule
- Surface dry 15 min, Walk-on dry 30 min, Overcoat min 4h, Cured 4h @ 23°C
Performance
- Heat Resistance
- 400°C continuous / 540°C peak
- Certificates & Approvals
- Pre-qualified NORSOK M-501. Complies with ASTM D520 type II zinc dust. RCSC Class B Appendix A.
Packaging
- Colours Available
- Greenish grey, grey
- Pack Sizes
- 8L Comp A (10L can) + 2.6L Zinc 100 Comp B (20L can)
- Shelf Life
- Comp A 6 months, Zinc 100 Comp B 48 months
Suitable Substrates
Environments
Related Products
Alkyd Coating
Pilot QD Primer
One-component alkyd primer with zinc phosphate. No mixing required — reducing waste, spills, and leftover paint. Dries quickly, forming a hard dry film in only 90 minutes, enabling rapid handling, stacking, and shipping of coated items.
Epoxy Primer
Penguard Express ZP
High-solids, high-build, fast-curing two-component epoxy primer pigmented with zinc phosphate. Designed for reliable anti-corrosion performance in atmospheric environments. Optimised for new construction with fast dry-to-recoat and dry-to-handle times. Low temperature application possible. Part of the Penguard range — over 650 million litres sold globally since the 1980s.
Epoxy Primer
Penguard Express MIO
Fast-drying, high-build epoxy coating reinforced with micaceous iron oxide (MIO) for increased barrier effect. Can be used as primer, midcoat, finish coat, or single-coat system in atmospheric conditions. Suitable up to C5 corrosivity. Fast dry-to-recoat and dry-to-handle. Can be applied at sub-zero surface temperatures.
Ready to Talk Coatings?
Our team is here to help with product selection, specifications, and technical support for your next project.